Leachate from a composting plant was characterized and applied as a biofertilizer in lettuce crops. Characteristics of untreated (UE) and anaerobically treated (TE) leachate samples were compared. The pH of TE (8.2) increased in relation to the UE (5.2) due to an increase in ammonia nitrogen in TE (1197 mg L-1) compared to UE (859 mg L-1). Anaerobic treatment was efficient in the removal of organic matter from the leachate, evaluated by the decrease of dissolved organic carbon, biochemical oxygen demand, total organic carbon and total solids. K presented the highest concentration (1743 mg L-1) in TE, followed by Mg (135 mg L-1). Cd, Pb and Cr were present at low concentrations in the samples, 0.047, 0.206 and 0.081 mg L-1, respectively. Salmonella, thermotolerant coliforms and viable helminth eggs were not present in TE, which was applied as a biofertilizer in a lettuce crop and compared to mineral fertilization based on fresh matter and dry matter production. Lettuce production using TE was statistically equivalent to mineral fertilization. Toxic metals were not detected in the lettuce shoots. It was concluded that the anaerobically treated leachate from the composting company has the potential to be used as a biofertilizer.

In this work, cellulose-based composite biofilms doped with silver nanoparticles (AgNPs) have been produced by eco-friendly process. The AgNPs were synthesized from Ilex paraguariensis with an average size of 45 nm, a characteristic plasmon band at 450 nm and zeta potential of -23 mV. The biofilm has been synthesized by casting method, using different volumes of AgNPs suspension with glycerol plasticizing agent (T6-T10) or not (T1-T5). The AgNPs were successfully incorporated into the biofilms, which was confirmed by scanning electron microscopy. The mechanical and optical structural and the antimicrobial properties of the biofilms have been determined. In the presence of AgNPs, the mechanical properties, thermal stability and water vapor barrier of the biofilms have not been altered. However, the addition of glycerol decreased the tensile strength and the modulus of elasticity, in addition to increasing the elongation of the biofilms and the water vapor barrier. The biofilm T10 showed a transmittance of ca. 10%, with high potential to be used as a UV light blocker. Finally, the biofilms doped with AgNPs showed activity against the bacterium Pseudomonas fluorescens. Given the above, this work presented a new biofilm with activity against the bacterium Pseudomonus fluorescens obtained by eco-friendly process.

In this work, alkaline and nickel-metal hydride spent batteries were used as precursors of metals for the synthesis of polymetallic materials. These materials were synthesized via chemical reduction. Materials produced from nickel-metal hydride spent batteries (PM-NiMH) have a nanometric size, whereas the alkaline spent batteries (PM-Alk) have a micrometric size. PM-NiMH consists mainly of Ni, Co, and Cu and the PM-Alk consists mainly of Mn and Zn. The surface areas of PM-NiMH and PM-Alk were 82 m2g-1 and 109 m2 g-1, respectively. The synthesized materials were applied in the removal of reactive blue dye 4 (RB4). Parameters such as initial pH of the system, dose of the materials, and initial concentration of the dye were optimized. For both materials, the removal capacity of RB4 was constant over a wide pH range of (4-10). The removal capacity increases with the decrease of the materials dose and increase of the dye concentration until saturation of the active sites. The RB4 removal by PM-NiMH occurs by adsorption and degradation processes, whereas PM-Alk occurs only by adsorptive processes. The RB4 removal process follows the Langmuir adsorption isotherm model with maximum removal capacities of 331 and 127 mg g-1 for PM-NiMH and PM-Alk, respectively.